Materials for

METHOD Logo large

Use the same polymers, composites, and metals found in familiar manufacturing processes ーfrom injection molding to machiningー thanks to METHOD’s unique environmental control features.

Polymers Category

LOW TEMPERATURE POLYMERS

Print complex mechanical assemblies with real production materials

Easy to use

52-49°C / 125-120°F

HDT (ASTM 648, 66 psi)

62 MPa / 8,990 psi

TSY (ASTM D638, 50 mm/min)

Durable and Easy

52-49°C / 125-120°F

HDT (ASTM 648, 66 psi)

35 MPa / 5,080 psi

TSY (ASTM D638, 50 mm/min)

Chemical Resistance

70°C / 158°F

HDT (ASTM 648, 66 psi)

44 MPa / 6,380 psi

TSY (ASTM D638, 50 mm/min)

Static Resistance

67.4°C / 89.6°F

HDT (ASTM 648, 66 psi)

38.8 / 5,511 psi

TSY (ASTM D638, 50 mm/min)

Abrasion Resistance

91°C / 196°F

HDT (ASTM 648, 66 psi)

66 MPa / 9,570 psi

TSY (ASTM D638, 50 mm/min)

Flexible

95

Durometer

93 MPa / 13,488 psi

TSY (ASTM D638, 50 mm/min)

High-temp nylon

80°C / 176°F

HDTA – 1.8 MPa

55 MPa / 7,977 psi

TSY (ISO527-2)

Polymers Category

HIGH TEMPERATURE POLYMERS

Print complex mechanical assemblies with real production materials

Improved ABS

84°C / 183°F

HDT (ASTM 648, 66 psi)

77 MPa / 11,167 psi

TSY (ASTM D638, 50 mm/min)

Popular MFG Material

52-49°C / 125-120°F

HDT (ASTM 648, 66 psi)

35 MPa / 5,080 psi

TSY (ASTM D638, 50 mm/min)

Popular MFG Material

< 106 Ohms/m²

Surface resistivity ASTM D257

35 MPa / 5,080 psi

TS ISO 527-2/1A/50

Popular MFG Material

107 - 109 Ohms/m²

Surface resistivity ASTM D257

24.3 MPa / 3,480 psi

TS ISO 527-2/1A/50

UV Resistance

70°C / 158°F

HDT (ASTM 648, 66 psi)

44 MPa / 6,380 psi

TSY (ASTM D638, 50 mm/min)

Translucent

67.4°C / 89.6°F

HDT (ASTM 648, 66 psi)

38.8 / 5,511 psi

TSY (ASTM D638, 50 mm/min)

Cold Temp Performance

91°C / 196°F

HDT (ASTM 648, 66 psi)

66 MPa / 9,570 psi

TSY (ASTM D638, 50 mm/min)

High Temp Durability

108°C / 226°F

ISO 306

37 MPa / 5,366 psi

ISO 527-2/5A/50

Flame Retardant

104°C / 219°F

ISO 306

60 MPa / 8,700 psi

ISO 527-2/5A/50

Translucent

119°C / 246°F

Vicat Softening

63 MPa / 9,137 psi

ISO 527-2/5A/50

Popular MFG Material

117°C / 242°F

Vicat Softening

59.7 MPa / 8658 psi

Tensile Strength

UL94 Flame retardant

116°C / 242°F

Vicat Softening

67 MPa / 9717 psi

Tensile Strength

Composites Category

COMPOSITES

Produce tools and end parts with improved strength, stiffness, and heat-deflection

Peak Strength

184°C / 363.2°F

HDT (ASTM 648, 66 psi)

110 MPa / 15,954.2 psi

TSY (ASTM D638, 50 mm/min)

Strength + Moisture Resistance

154°C / 309.2°F

HDT (ASTM 648, 66 psi)

66 MPa / 9,572 psi

TSY (ASTM D638, 50 mm/min)

N/A

HDT (ASTM 648, 66 psi)

35.7 MPa / 5,177 psi

ISO 527-2/5A/50

Durable Strength

N/A

HDT (ASTM 648, 66 psi)

30 MPa / 4,351 psi

ISO 527-2/5A/50

Rigid Chem Resistance

HDT (ASTM 648, 66 psi)

N/A

92.9 MPa / 13,488 psi

ISO 527-2/5A/50

Strong and stiff

N/A

HDT (ISO 75)

130 MPa / 18,854 psi

ISO 527-2/5A/50

Heat Resistance

125°C / 257°F

ST (MPTS ISO 3167)

80 MPa / 11,603 psi

TSY (ASTM D638, 50 mm/min)

Metals Category

METALS

Print real metal components and tools when nothing else will do

7850 kg/m3

Sintered density

561 MPa / 81,366 psi

ISO 6892-1

Rapid rinse 2 impellers

Soluble supports

Print parts true-to-design with unlimited geometric freedom and easy post-processing

WATER SOLUBLE

Support Extruder 2XA

WATER SOLUBLE

Support Extruder 2A

Soluble

Support Extruder 2XA

FREE DOWNLOAD

The 2021 Guide to 3D Printing Materials

METHOD Logo large

Extruders

4-in-1 and 6-in-1 modular extruders allow for quick change between material groups, preventing cross-contamination.

Extruders & Material Compatibility

MODEL 1A Extruder

Available on:

SUPPORT 2A Extruder

Available on:

METHOD Logo large

PLATFORM

Limitless 3D Printing.
Unlock innovation with the most advanced professional 3D printing platform available.

Industry Applications

Industrial reliability and precision at a disruptive price point with the fastest CAD to part workflow.

<